Submerged Arc Welding Wire

H08A (AWS EL8) used for automatic submerged arc welding low carbon steel and some low-alloy steel structures (such as 16Mn), do with high Mn type welding flux.
H08MnA (AWS EM12) for welding carbon steel and low-alloy steel structures of relevant strength grade along with flux.
H10Mn2 (AWS EH14) used for automatic submerged arc welding carbon steel and low-alloy steel, such as 16Mn, 14MnNb welding structures.

Welding Wire Chemical Composition(%)



C
Mn
Si
S
P
Cu
H08AAWS EL8≤0.100.30-0.60≤0.03≤0.030≤0.030≤0.20
H08MnAAWS EM12≤0.100.80-1.10≤0.07≤0.030≤0.030≤0.20
H10Mn2AWS EH14≤0.121.50-1.90≤0.07≤0.030≤0.030≤0.20


Mechanical Properties of Deposited Metal:


Yield Strength (Mpa)Tensile Strength (Mpa)Extension rate (%)Shock value (-40℃)
H08A425
545
30
87
H08MnA465
555
30
40
H10Mn2465
560
32
47


Specification and Reference Current:

Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Current(A)300-400350-450425-525475-575550-650


Applicable to welding of low-carbon steel and come low-alloy steel (such as 16Mn), automatic submerged arc welding of boilers, pressure vessels, etc.
 
The products easily removable residue, good seam forming and highly efficient deposition. Wire melting doesnot lead to splash or strong flashing. The seam surface is smooth and welding quality is guaranteed. They facilitate mechanical and automatic welding process. With a wide range of welding parameters, the wires can be used in open fields with strong wind and applied to automobiles, ships, bridges, and chemical engineering.

LinksWelding Electrode Welding Wire Submerged Arc Welding Wire Flux Cored Welding Wire Welding Torch

HomeProductsNewsAbout UsContact UsSitemap

manager@hbaining.com+86 133 6380 3091No.313 East Of Heping Road,Shijiazhuang,China

Copyright © Hebei Aining Welding Consumable Co., Ltd. All Rights Reserved. Technical Support: Reanod.

Jake Song

Ms.Vicky

Ms.Eva

Ms.Amy

Tel: +86-311-6669 7109

manager@hbaining.com
Hebei Welding Consumable Supplier
HomeProductsSubmerged Arc Welding Wire
Welding Electrode Stainless Steel Welding Electrode CO2 Welding Wire Submerged Arc Welding Wire Argon Arc Welding Wire Flux Cored Welding Wire Welding Torch Copper Coated Carbon Electrodes Aluminum Welding Wire Stainless Steel Welding Wire Cast Iron Welding Electrode Cuttiing and Grinding Wheels Welding Gloves
Submerged Arc Welding Wire

Product Name: Submerged Arc Welding Wire

Specification: 2.0MM, 2.4MM, 3.0MM

Delivery Time: 10 days

Payment Term: T/T or L/C

Submerged Arc Welding Wire

H08A (AWS EL8) used for automatic submerged arc welding low carbon steel and some low-alloy steel structures (such as 16Mn), do with high Mn type welding flux.
H08MnA (AWS EM12) for welding carbon steel and low-alloy steel structures of relevant strength grade along with flux.
H10Mn2 (AWS EH14) used for automatic submerged arc welding carbon steel and low-alloy steel, such as 16Mn, 14MnNb welding structures.

Welding Wire Chemical Composition(%)



C
Mn
Si
S
P
Cu
H08AAWS EL8≤0.100.30-0.60≤0.03≤0.030≤0.030≤0.20
H08MnAAWS EM12≤0.100.80-1.10≤0.07≤0.030≤0.030≤0.20
H10Mn2AWS EH14≤0.121.50-1.90≤0.07≤0.030≤0.030≤0.20


Mechanical Properties of Deposited Metal:


Yield Strength (Mpa)Tensile Strength (Mpa)Extension rate (%)Shock value (-40℃)
H08A425
545
30
87
H08MnA465
555
30
40
H10Mn2465
560
32
47


Specification and Reference Current:

Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Current(A)300-400350-450425-525475-575550-650


Applicable to welding of low-carbon steel and come low-alloy steel (such as 16Mn), automatic submerged arc welding of boilers, pressure vessels, etc.
 
The products easily removable residue, good seam forming and highly efficient deposition. Wire melting doesnot lead to splash or strong flashing. The seam surface is smooth and welding quality is guaranteed. They facilitate mechanical and automatic welding process. With a wide range of welding parameters, the wires can be used in open fields with strong wind and applied to automobiles, ships, bridges, and chemical engineering.

Home |Products|Quality Control|News|About Us|Contact Us

+86 133 6380 3091

manager@hbaining.com

No.313 East Of Heping Road,Shijiazhuang,China

Copyright © Hebei Aining Welding Consumable Co., Ltd.

All Rights Reserved. Technical Support: Reanod.

Welding Consumable Supplier

E-mail: manager@hbaining.com

Home Products Quality Control News About Us Contact Us
HomeProductsSubmerged Arc Welding Wire
Welding Electrode Stainless Steel Welding Electrode CO2 Welding Wire Submerged Arc Welding Wire Argon Arc Welding Wire Flux Cored Welding Wire Welding Torch Copper Coated Carbon Electrodes Aluminum Welding Wire Stainless Steel Welding Wire Cast Iron Welding Electrode Cuttiing and Grinding Wheels Welding Gloves
Submerged Arc Welding Wire

Product Name: Submerged Arc Welding Wire

Specification: 2.0MM, 2.4MM, 3.0MM

Delivery Time: 10 days

Payment Term: T/T or L/C

Submerged Arc Welding Wire

H08A (AWS EL8) used for automatic submerged arc welding low carbon steel and some low-alloy steel structures (such as 16Mn), do with high Mn type welding flux.
H08MnA (AWS EM12) for welding carbon steel and low-alloy steel structures of relevant strength grade along with flux.
H10Mn2 (AWS EH14) used for automatic submerged arc welding carbon steel and low-alloy steel, such as 16Mn, 14MnNb welding structures.

Welding Wire Chemical Composition(%)



C
Mn
Si
S
P
Cu
H08AAWS EL8≤0.100.30-0.60≤0.03≤0.030≤0.030≤0.20
H08MnAAWS EM12≤0.100.80-1.10≤0.07≤0.030≤0.030≤0.20
H10Mn2AWS EH14≤0.121.50-1.90≤0.07≤0.030≤0.030≤0.20


Mechanical Properties of Deposited Metal:


Yield Strength (Mpa)Tensile Strength (Mpa)Extension rate (%)Shock value (-40℃)
H08A425
545
30
87
H08MnA465
555
30
40
H10Mn2465
560
32
47


Specification and Reference Current:

Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Current(A)300-400350-450425-525475-575550-650


Applicable to welding of low-carbon steel and come low-alloy steel (such as 16Mn), automatic submerged arc welding of boilers, pressure vessels, etc.
 
The products easily removable residue, good seam forming and highly efficient deposition. Wire melting doesnot lead to splash or strong flashing. The seam surface is smooth and welding quality is guaranteed. They facilitate mechanical and automatic welding process. With a wide range of welding parameters, the wires can be used in open fields with strong wind and applied to automobiles, ships, bridges, and chemical engineering.

Home |Products|Quality Control|News|About Us|Contact Us

manager@hbaining.com+86 133 6380 3091

No.313 East Of Heping Road,Shijiazhuang,China

Copyright © Hebei Aining Welding Consumable Co., Ltd. All Rights Reserved. Technical Support: Reanod.