Enquire NowMild Steel welding electrode / welding rod E7016 has a coating with low-content hydrogen and sodium. It has excellent plasticity, tenacity and anti-cracking ability in low temperature, good arc stiffness, nearly no magnetic blow. Therefore, it can offer good minor parts in welding with very few splash and easy deslagging and stable electric arc. Good deslagging is the technical advantage of our company.
Welding electrode / welding rod E7016 application:
It is widely used for welding materials of carbon steel and low alloy steel, like 16Mn, and welding Grade A, B, D, E steel for shipyard primary components, boiler, pressure vessels, pipelines, and other important steel structure components.
Attention:
Before usage, welding electrodes should be dried in 350℃ for an hour and used shortly after being dried.
Impurities like oil, rust, water and so on must be removed before usage.
Short arc welding and narrow path welding are adoptive.
Chemical Composition of Deposited Metal (%)
| C | Mn | Si | S | P | Cr | Ni*Mo |
| - | ≤1.60 | ≤0.75 | ≤0.035 | ≤0.040 | ≤0.20 | ≤0.30 |
Recommended Welding Currents:
| Diameter(mm) | 2.0 | 2.5 | 3.2 | 4.0 | 5.0 | 5.8 |
| Length(mm) | 300 | 300 | 350 | 400 | 400 | 400 |
| Welding Current(A) | 50-80 | 70-110 | 100-140 | 150-180 | 180-230 | 230-260 |
Mechanical Properties of Deposited Metal:
| Rm(Mpa) | Rel(Mpa) | A(%) | Akv(J) |
| ≥490 | ≥400 | ≥22 | ≥27 |
Home丨Products丨News丨About Us丨Contact Us丨Sitemap
manager@hbaining.com+86 133 6380 3091No.313 East Of Heping Road,Shijiazhuang,China
Copyright © Hebei Aining Welding Consumable Co., Ltd. All Rights Reserved. Technical Support: Reanod.
Specification: 2.5*300MM, 3.2*350MM, 4.0*400MM
Delivery Time: 10 days
Payment Term: T/T or L/C
Mild Steel welding electrode / welding rod E7016 has a coating with low-content hydrogen and sodium. It has excellent plasticity, tenacity and anti-cracking ability in low temperature, good arc stiffness, nearly no magnetic blow. Therefore, it can offer good minor parts in welding with very few splash and easy deslagging and stable electric arc. Good deslagging is the technical advantage of our company.
Welding electrode / welding rod E7016 application:
It is widely used for welding materials of carbon steel and low alloy steel, like 16Mn, and welding Grade A, B, D, E steel for shipyard primary components, boiler, pressure vessels, pipelines, and other important steel structure components.
Attention:
Before usage, welding electrodes should be dried in 350℃ for an hour and used shortly after being dried.
Impurities like oil, rust, water and so on must be removed before usage.
Short arc welding and narrow path welding are adoptive.
Chemical Composition of Deposited Metal (%)
| C | Mn | Si | S | P | Cr | Ni*Mo |
| - | ≤1.60 | ≤0.75 | ≤0.035 | ≤0.040 | ≤0.20 | ≤0.30 |
Recommended Welding Currents:
| Diameter(mm) | 2.0 | 2.5 | 3.2 | 4.0 | 5.0 | 5.8 |
| Length(mm) | 300 | 300 | 350 | 400 | 400 | 400 |
| Welding Current(A) | 50-80 | 70-110 | 100-140 | 150-180 | 180-230 | 230-260 |
Mechanical Properties of Deposited Metal:
| Rm(Mpa) | Rel(Mpa) | A(%) | Akv(J) |
| ≥490 | ≥400 | ≥22 | ≥27 |
Home |Products|Quality Control|News|About Us|Contact Us
+86 133 6380 3091
No.313 East Of Heping Road,Shijiazhuang,China
Copyright © Hebei Aining Welding Consumable Co., Ltd.
All Rights Reserved. Technical Support: Reanod.
E-mail: manager@hbaining.com
Specification: 2.5*300MM, 3.2*350MM, 4.0*400MM
Delivery Time: 10 days
Payment Term: T/T or L/C
Mild Steel welding electrode / welding rod E7016 has a coating with low-content hydrogen and sodium. It has excellent plasticity, tenacity and anti-cracking ability in low temperature, good arc stiffness, nearly no magnetic blow. Therefore, it can offer good minor parts in welding with very few splash and easy deslagging and stable electric arc. Good deslagging is the technical advantage of our company.
Welding electrode / welding rod E7016 application:
It is widely used for welding materials of carbon steel and low alloy steel, like 16Mn, and welding Grade A, B, D, E steel for shipyard primary components, boiler, pressure vessels, pipelines, and other important steel structure components.
Attention:
Before usage, welding electrodes should be dried in 350℃ for an hour and used shortly after being dried.
Impurities like oil, rust, water and so on must be removed before usage.
Short arc welding and narrow path welding are adoptive.
Chemical Composition of Deposited Metal (%)
| C | Mn | Si | S | P | Cr | Ni*Mo |
| - | ≤1.60 | ≤0.75 | ≤0.035 | ≤0.040 | ≤0.20 | ≤0.30 |
Recommended Welding Currents:
| Diameter(mm) | 2.0 | 2.5 | 3.2 | 4.0 | 5.0 | 5.8 |
| Length(mm) | 300 | 300 | 350 | 400 | 400 | 400 |
| Welding Current(A) | 50-80 | 70-110 | 100-140 | 150-180 | 180-230 | 230-260 |
Mechanical Properties of Deposited Metal:
| Rm(Mpa) | Rel(Mpa) | A(%) | Akv(J) |
| ≥490 | ≥400 | ≥22 | ≥27 |
Home |Products|Quality Control|News|About Us|Contact Us
manager@hbaining.com+86 133 6380 3091
No.313 East Of Heping Road,Shijiazhuang,China
Copyright © Hebei Aining Welding Consumable Co., Ltd. All Rights Reserved. Technical Support: Reanod.