E7018 Welding Electrode

Specification: 3.2*350MM, 4.0*400MM

Delivery Time:10 days

Payment Term: T/T or L/C

Inquire Now

E7018 Welding Electrode is an outstanding quality all position welding electrode, covered with extra low hydrogen potassium type, coating for welding high tensile steels and low alloy steels. Its nominal welding efficiency is about 110% due to iron powder is contained. The weld metal shows an excellent low temperature toughness and high crack resistance. Ti is widely used in important projects of ships, boilers, high press vessel, bridges, skyscrapers, offshore drilling platforms, nuclear power stations ect. The groove of base metal should be cleared away impurities, and the electrode must be baked at a temperature to 400 degree, then be held 1-2 hours before welding, 2.5mm one should be done by 350 degree, then be held 1 hour.

The normal sizes: 2.5*300mm, 3.2*350mm, 4.0*400mm, 5.0*450mm.

Chemical Composition of Deposited Metal (%):

	C	Mn	Si	S	P	Cr	Ni	Mo	V
Standard	≤0.15	≤1.60	≤0.75	≤0.035	≤0.040	≤0.20	≤0.30	≤0.30	≤0.08
Typical	0.068	1.36	0.51	0.010	0.016	0.047	0.022	0.010	0.014

Mechanical Properties of Deposited Metal (%)

	Yield Point ReH (Mpa)	Tensile Strength Rm (Mpa)	Elongation A 5 (%)	-20℃(J)	-29℃(J)	-46℃(J)
Standard	≥375	490-660	≥22	≥47	≥27	≥27
Gypical	440	540	30	170	150	130

The normal sizes: 2.5*300mm, 3.2*350mm, 4.0*400mm, 5.0*450mm.

Chemical Composition of Deposited Metal (%):

	C	Mn	Si	S	P	Cr	Ni	Mo	V
Standard	≤0.15	≤1.60	≤0.75	≤0.035	≤0.040	≤0.20	≤0.30	≤0.30	≤0.08
Typical	0.068	1.36	0.51	0.010	0.016	0.047	0.022	0.010	0.014

Mechanical Properties of Deposited Metal (%)

	Yield Point ReH (Mpa)	Tensile Strength Rm (Mpa)	Elongation A 5 (%)	-20℃(J)	-29℃(J)	-46℃(J)
Standard	≥375	490-660	≥22	≥47	≥27	≥27
Gypical	440	540	30	170	150	130

Home 丨Products丨Quality Control丨News丨About Us丨Contact Us

manager@hbaining.com +86 133 6380 3091 No.313 East Of Heping Road,Shijiazhuang,China

+86 133 6380 3091

manager@hbaining.com

No.313 East Of Heping Road,Shijiazhuang,China

The normal sizes: 2.5*300mm, 3.2*350mm, 4.0*400mm, 5.0*450mm.

Chemical Composition of Deposited Metal (%):

	C	Mn	Si	S	P	Cr	Ni	Mo	V
Standard	≤0.15	≤1.60	≤0.75	≤0.035	≤0.040	≤0.20	≤0.30	≤0.30	≤0.08
Typical	0.068	1.36	0.51	0.010	0.016	0.047	0.022	0.010	0.014

Mechanical Properties of Deposited Metal (%)

	Yield Point ReH (Mpa)	Tensile Strength Rm (Mpa)	Elongation A 5 (%)	-20℃(J)	-29℃(J)	-46℃(J)
Standard	≥375	490-660	≥22	≥47	≥27	≥27
Gypical	440	540	30	170	150	130

E7018 Welding Electrode

Product Name: E7018 Welding Electrode

Product Name: E7018 Welding Electrode