Mobile Website 
Product Name:
Specification: 2.5*300mm, 3.2*350mm
Delivery Time:15 days
Payment Term: T/T or LC
Inquire NowZ208
Accord with：GB/T 10044 EZC
Description:
Z208 cast iron welding electrode is a graphitic type coating cast iron electrode with carbon steel core. Both AC and DC can be applied in welding. Weld seam metal has excellent crack resistibility. And its price is cheaper.
Applications:
It is used for repairing welding defects for gray cast iron.
Chemical Composition of Deposited Metal: (%)
C | Mn | Si | S | P | Fe | |
Standard | 2.00-4.00 | ≤0.75 | 2.50-6.50 | ≤0.10 | ≤0.15 | The rest |
Typical | 2.70 | 0.40 | 4.20 | 0.006 | 0.020 |
Recommended Current (AC or DC)
Size(mm) | 2.5*300 | 3.2*350 | 4.0*400 | 5.0*400 |
Current(A) | 60-90 | 90-120 | 150-180 | 190-220 |
Attention:
a. welding electrodes must be baked for 1 hour at the temperature of 150℃ before welding.
b. For cast iron parts bearing impact stress, it is not good to use it.
c. For welding detects of small and thin cast iron parts fabricated by low steel, welding electrodes need not be preheated. For general welding pipes, welding electrodes should be preheated to around 400℃, cool it after welding and the welding zone may be processed by cutting.
Home 丨Products丨Quality Control丨News丨About Us丨Contact Us 丨Sitemap
manager@hbaining.com +86 133 6380 3091 No.313 East Of Heping Road,Shijiazhuang,China
Copyright © Hebei Aining Welding Consumable Co., Ltd. Technical Support: Reanod
Specification: 2.5*300mm, 3.2*350mm
Delivery Time: 15 days
Payment Term:T/T or LC
Z208
Accord with：GB/T 10044 EZC
Description:
Z208 cast iron welding electrode is a graphitic type coating cast iron electrode with carbon steel core. Both AC and DC can be applied in welding. Weld seam metal has excellent crack resistibility. And its price is cheaper.
Applications:
It is used for repairing welding defects for gray cast iron.
Chemical Composition of Deposited Metal: (%)
C | Mn | Si | S | P | Fe | |
Standard | 2.00-4.00 | ≤0.75 | 2.50-6.50 | ≤0.10 | ≤0.15 | The rest |
Typical | 2.70 | 0.40 | 4.20 | 0.006 | 0.020 |
Recommended Current (AC or DC)
Size(mm) | 2.5*300 | 3.2*350 | 4.0*400 | 5.0*400 |
Current(A) | 60-90 | 90-120 | 150-180 | 190-220 |
Attention:
a. welding electrodes must be baked for 1 hour at the temperature of 150℃ before welding.
b. For cast iron parts bearing impact stress, it is not good to use it.
c. For welding detects of small and thin cast iron parts fabricated by low steel, welding electrodes need not be preheated. For general welding pipes, welding electrodes should be preheated to around 400℃, cool it after welding and the welding zone may be processed by cutting.
Home 丨Products丨Quality Control丨News丨About Us丨Contact Us
manager@hbaining.com +86 133 6380 3091 No.313 East Of Heping Road,Shijiazhuang,China
+86 133 6380 3091
No.313 East Of Heping Road,Shijiazhuang,China
No.313 East Of Heping Road,Shijiazhuang,China
Copyright © Hebei Aining Welding Consumable Co., Ltd.
All Rights Reserved. Technical Support: Reanod
Specification: 2.5*300mm, 3.2*350mm
Delivery Time: 15 days
Payment Term:T/T or LC
Z208
Accord with：GB/T 10044 EZC
Description:
Z208 cast iron welding electrode is a graphitic type coating cast iron electrode with carbon steel core. Both AC and DC can be applied in welding. Weld seam metal has excellent crack resistibility. And its price is cheaper.
Applications:
It is used for repairing welding defects for gray cast iron.
Chemical Composition of Deposited Metal: (%)
C | Mn | Si | S | P | Fe | |
Standard | 2.00-4.00 | ≤0.75 | 2.50-6.50 | ≤0.10 | ≤0.15 | The rest |
Typical | 2.70 | 0.40 | 4.20 | 0.006 | 0.020 |
Recommended Current (AC or DC)
Size(mm) | 2.5*300 | 3.2*350 | 4.0*400 | 5.0*400 |
Current(A) | 60-90 | 90-120 | 150-180 | 190-220 |
Attention:
a. welding electrodes must be baked for 1 hour at the temperature of 150℃ before welding.
b. For cast iron parts bearing impact stress, it is not good to use it.
c. For welding detects of small and thin cast iron parts fabricated by low steel, welding electrodes need not be preheated. For general welding pipes, welding electrodes should be preheated to around 400℃, cool it after welding and the welding zone may be processed by cutting.
Home 丨Products丨Quality Control丨News丨About Us丨Contact Us
manager@hbaining.com +86 133 6380 3091
No.313 East Of Heping Road,Shijiazhuang,China
Copyright © Hebei Aining Welding Consumable Co., Ltd. Technical Support: Reanod