Inquire NowZ308
Accord with：GB/T 10044 EZNi-1
Equivalent norm: AWS A5.15 ENi-C1
Description:
Z308 cast iron welding electrode is a covered welding electrode with pure nickel core and graphitic coating for cast iron. The Weld seam metal has excellent machinability and crack resistibility. Both AC and DC can be applied.
Applications:
It is used for repairing welding thin pieces and processing surface of cast iron, as well as important grey cast iron pieces, such as engine gear box, machining tools, guideway, etc
Chemical Composition of Deposited Metal: (%)
C | Mn | Si | S | Ni | Fe | Others | |
Standard | ≤2.0 | ≤1.0 | ≤2.50 | ≤0.03 | ≥90 | ≤8.0 | ≤1.0 |
Typical | 0.59 | 0.07 | 1.50 | 0.004 | 94 | 0.021 |
Recommended Current (AC or DC)
Size(mm) | 2.5*300 | 3.2*350 | 4.0*400 | 5.0*400 |
Current(A) | 60-90 | 90-110 | 120-150 | 150-180 |
Attention:
a. welding electrodes must be baked for 1 hour at the temperature of 80-120℃ before welding.
b. Hammering the welded seam to dispel stress around the welding region and to avoid cracking.
c. Large current should be avoided in cold welding for cast iron, so as to reduce impurities of base metal to penetrate the weld seam and to reduce the width of the weld zone, and then to improve the ability of crack-resistance and capability of machine processing of the weld seam.
Home 丨Products丨Quality Control丨News丨About Us丨Contact Us 丨Sitemap
manager@hbaining.com +86 133 6380 3091 No.313 East Of Heping Road,Shijiazhuang,China
Copyright © Hebei Aining Welding Consumable Co., Ltd. Technical Support: Reanod
Specification: 3.2*350mm, 4.0*400mm
Delivery Time: 15 days
Payment Term:T/T or LC
Z308
Accord with：GB/T 10044 EZNi-1
Equivalent norm: AWS A5.15 ENi-C1
Description:
Z308 cast iron welding electrode is a covered welding electrode with pure nickel core and graphitic coating for cast iron. The Weld seam metal has excellent machinability and crack resistibility. Both AC and DC can be applied.
Applications:
It is used for repairing welding thin pieces and processing surface of cast iron, as well as important grey cast iron pieces, such as engine gear box, machining tools, guideway, etc
Chemical Composition of Deposited Metal: (%)
C | Mn | Si | S | Ni | Fe | Others | |
Standard | ≤2.0 | ≤1.0 | ≤2.50 | ≤0.03 | ≥90 | ≤8.0 | ≤1.0 |
Typical | 0.59 | 0.07 | 1.50 | 0.004 | 94 | 0.021 |
Recommended Current (AC or DC)
Size(mm) | 2.5*300 | 3.2*350 | 4.0*400 | 5.0*400 |
Current(A) | 60-90 | 90-110 | 120-150 | 150-180 |
Attention:
a. welding electrodes must be baked for 1 hour at the temperature of 80-120℃ before welding.
b. Hammering the welded seam to dispel stress around the welding region and to avoid cracking.
c. Large current should be avoided in cold welding for cast iron, so as to reduce impurities of base metal to penetrate the weld seam and to reduce the width of the weld zone, and then to improve the ability of crack-resistance and capability of machine processing of the weld seam.
Home 丨Products丨Quality Control丨News丨About Us丨Contact Us
manager@hbaining.com +86 133 6380 3091 No.313 East Of Heping Road,Shijiazhuang,China
+86 133 6380 3091
No.313 East Of Heping Road,Shijiazhuang,China
No.313 East Of Heping Road,Shijiazhuang,China
Copyright © Hebei Aining Welding Consumable Co., Ltd.
All Rights Reserved. Technical Support: Reanod
Specification: 3.2*350mm, 4.0*400mm
Delivery Time: 15 days
Payment Term:T/T or LC
Z308
Accord with：GB/T 10044 EZNi-1
Equivalent norm: AWS A5.15 ENi-C1
Description:
Z308 cast iron welding electrode is a covered welding electrode with pure nickel core and graphitic coating for cast iron. The Weld seam metal has excellent machinability and crack resistibility. Both AC and DC can be applied.
Applications:
It is used for repairing welding thin pieces and processing surface of cast iron, as well as important grey cast iron pieces, such as engine gear box, machining tools, guideway, etc
Chemical Composition of Deposited Metal: (%)
C | Mn | Si | S | Ni | Fe | Others | |
Standard | ≤2.0 | ≤1.0 | ≤2.50 | ≤0.03 | ≥90 | ≤8.0 | ≤1.0 |
Typical | 0.59 | 0.07 | 1.50 | 0.004 | 94 | 0.021 |
Recommended Current (AC or DC)
Size(mm) | 2.5*300 | 3.2*350 | 4.0*400 | 5.0*400 |
Current(A) | 60-90 | 90-110 | 120-150 | 150-180 |
Attention:
a. welding electrodes must be baked for 1 hour at the temperature of 80-120℃ before welding.
b. Hammering the welded seam to dispel stress around the welding region and to avoid cracking.
c. Large current should be avoided in cold welding for cast iron, so as to reduce impurities of base metal to penetrate the weld seam and to reduce the width of the weld zone, and then to improve the ability of crack-resistance and capability of machine processing of the weld seam.
Home 丨Products丨Quality Control丨News丨About Us丨Contact Us
manager@hbaining.com +86 133 6380 3091
No.313 East Of Heping Road,Shijiazhuang,China
Copyright © Hebei Aining Welding Consumable Co., Ltd. Technical Support: Reanod