Enquire NowZ508
Accord with：GB/T 10044 EZNiCu-1
Equivalent norm: AWS A5.15 ENiCu-B
Description:
Z508 cast iron welding electrode is a graphitic (with strong reducing) type coating with Cu-Ni alloy (Monel) core welding electrodes for cast iron. Its technology properties and machinabilities are both close to those of Z308 and it is not suitable for welding pressed position, but suitable for welding gray cast iron.
Applications:
It is used for repairing welding gray iron casting strength of which is not so highly required.
Chemical Composition of Deposited Metal: (%)
C | Mn | Si | S | Ni | Fe | Cu | |
Standard | 0.35-0.55 | ≤2.30 | ≤0.75 | ≤0.025 | 60-70 | 3.0-6.0 | 23-35 |
Typical | 0.45 | 1.10 | 0.55 | 0.006 | 64 | 4.0 | 28 |
Recommended Current (AC or DC)
Size(mm) | 3.2*350 | 4.0*400 | 5.0*400 |
Current(A) | 90-110 | 120-150 | 160-190 |
Attention:
a. welding electrodes must be baked for 1 hour at the temperature of 150℃ before welding.
b. When welding, narrow weld seam is recommended and its length should be less than 50mm, and after welding, hammer the weld metal immediately to dispel stress around the welding region and avoid cracking.
Home丨Products丨News丨About Us丨Contact Us丨Sitemap
manager@hbaining.com+86 133 6380 3091No.313 East Of Heping Road,Shijiazhuang,China
Copyright © Hebei Aining Welding Consumable Co., Ltd. All Rights Reserved. Technical Support: Reanod.
Specification: 3.2*350mm, 4.0*400mm
Delivery Time: 15 days
Payment Term: TT or LC
Z508
Accord with：GB/T 10044 EZNiCu-1
Equivalent norm: AWS A5.15 ENiCu-B
Description:
Z508 cast iron welding electrode is a graphitic (with strong reducing) type coating with Cu-Ni alloy (Monel) core welding electrodes for cast iron. Its technology properties and machinabilities are both close to those of Z308 and it is not suitable for welding pressed position, but suitable for welding gray cast iron.
Applications:
It is used for repairing welding gray iron casting strength of which is not so highly required.
Chemical Composition of Deposited Metal: (%)
C | Mn | Si | S | Ni | Fe | Cu | |
Standard | 0.35-0.55 | ≤2.30 | ≤0.75 | ≤0.025 | 60-70 | 3.0-6.0 | 23-35 |
Typical | 0.45 | 1.10 | 0.55 | 0.006 | 64 | 4.0 | 28 |
Recommended Current (AC or DC)
Size(mm) | 3.2*350 | 4.0*400 | 5.0*400 |
Current(A) | 90-110 | 120-150 | 160-190 |
Attention:
a. welding electrodes must be baked for 1 hour at the temperature of 150℃ before welding.
b. When welding, narrow weld seam is recommended and its length should be less than 50mm, and after welding, hammer the weld metal immediately to dispel stress around the welding region and avoid cracking.
Home |Products|Quality Control|News|About Us|Contact Us
+86 133 6380 3091
No.313 East Of Heping Road,Shijiazhuang,China
Copyright © Hebei Aining Welding Consumable Co., Ltd.
All Rights Reserved. Technical Support: Reanod.
E-mail: manager@hbaining.com
Specification: 3.2*350mm, 4.0*400mm
Delivery Time: 15 days
Payment Term: TT or LC
Z508
Accord with：GB/T 10044 EZNiCu-1
Equivalent norm: AWS A5.15 ENiCu-B
Description:
Z508 cast iron welding electrode is a graphitic (with strong reducing) type coating with Cu-Ni alloy (Monel) core welding electrodes for cast iron. Its technology properties and machinabilities are both close to those of Z308 and it is not suitable for welding pressed position, but suitable for welding gray cast iron.
Applications:
It is used for repairing welding gray iron casting strength of which is not so highly required.
Chemical Composition of Deposited Metal: (%)
C | Mn | Si | S | Ni | Fe | Cu | |
Standard | 0.35-0.55 | ≤2.30 | ≤0.75 | ≤0.025 | 60-70 | 3.0-6.0 | 23-35 |
Typical | 0.45 | 1.10 | 0.55 | 0.006 | 64 | 4.0 | 28 |
Recommended Current (AC or DC)
Size(mm) | 3.2*350 | 4.0*400 | 5.0*400 |
Current(A) | 90-110 | 120-150 | 160-190 |
Attention:
a. welding electrodes must be baked for 1 hour at the temperature of 150℃ before welding.
b. When welding, narrow weld seam is recommended and its length should be less than 50mm, and after welding, hammer the weld metal immediately to dispel stress around the welding region and avoid cracking.
Home |Products|Quality Control|News|About Us|Contact Us
manager@hbaining.com+86 133 6380 3091
No.313 East Of Heping Road,Shijiazhuang,China
Copyright © Hebei Aining Welding Consumable Co., Ltd. All Rights Reserved. Technical Support: Reanod.