Mobile Website 
Product Name:
Specification: 3.2*350MM, 4.0*400MM
Delivery Time:10 days
Payment Term: T/T or L/C
Enquire NowE7018 Welding Electrode is an outstanding quality all position welding electrode, covered with extra low hydrogen potassium type, coating for welding high tensile steels and low alloy steels. Its nominal welding efficiency is about 110% due to iron powder is contained. The weld metal shows an excellent low temperature toughness and high crack resistance. Ti is widely used in important projects of ships, boilers, high press vessel, bridges, skyscrapers, offshore drilling platforms, nuclear power stations ect. The groove of base metal should be cleared away impurities, and the electrode must be baked at a temperature to 400 degree, then be held 1-2 hours before welding, 2.5mm one should be done by 350 degree, then be held 1 hour.
The normal sizes: 2.5*300mm, 3.2*350mm, 4.0*400mm, 5.0*450mm.
Chemical Composition of Deposited Metal (%):
| C | Mn | Si | S | P | Cr | Ni | Mo | V | |
| Standard | ≤0.15 | ≤1.60 | ≤0.75 | ≤0.035 | ≤0.040 | ≤0.20 | ≤0.30 | ≤0.30 | ≤0.08 |
| Typical | 0.068 | 1.36 | 0.51 | 0.010 | 0.016 | 0.047 | 0.022 | 0.010 | 0.014 |
Mechanical Properties of Deposited Metal (%)
| Yield Point ReH (Mpa) | Tensile Strength Rm (Mpa) | Elongation A 5 (%) | -20℃(J) | -29℃(J) | -46℃(J) | |
| Standard | ≥375 | 490-660 | ≥22 | ≥47 | ≥27 | ≥27 |
| Gypical | 440 | 540 | 30 | 170 | 150 | 130 |
Home丨Products丨News丨About Us丨Contact Us丨Sitemap
manager@hbaining.com+86 133 6380 3091No.313 East Of Heping Road,Shijiazhuang,China
Copyright © Hebei Aining Welding Consumable Co., Ltd. All Rights Reserved. Technical Support: Reanod.
Specification: 3.2*350MM, 4.0*400MM
Delivery Time: 10 days
Payment Term: T/T or L/C
E7018 Welding Electrode is an outstanding quality all position welding electrode, covered with extra low hydrogen potassium type, coating for welding high tensile steels and low alloy steels. Its nominal welding efficiency is about 110% due to iron powder is contained. The weld metal shows an excellent low temperature toughness and high crack resistance. Ti is widely used in important projects of ships, boilers, high press vessel, bridges, skyscrapers, offshore drilling platforms, nuclear power stations ect. The groove of base metal should be cleared away impurities, and the electrode must be baked at a temperature to 400 degree, then be held 1-2 hours before welding, 2.5mm one should be done by 350 degree, then be held 1 hour.
The normal sizes: 2.5*300mm, 3.2*350mm, 4.0*400mm, 5.0*450mm.
Chemical Composition of Deposited Metal (%):
| C | Mn | Si | S | P | Cr | Ni | Mo | V | |
| Standard | ≤0.15 | ≤1.60 | ≤0.75 | ≤0.035 | ≤0.040 | ≤0.20 | ≤0.30 | ≤0.30 | ≤0.08 |
| Typical | 0.068 | 1.36 | 0.51 | 0.010 | 0.016 | 0.047 | 0.022 | 0.010 | 0.014 |
Mechanical Properties of Deposited Metal (%)
| Yield Point ReH (Mpa) | Tensile Strength Rm (Mpa) | Elongation A 5 (%) | -20℃(J) | -29℃(J) | -46℃(J) | |
| Standard | ≥375 | 490-660 | ≥22 | ≥47 | ≥27 | ≥27 |
| Gypical | 440 | 540 | 30 | 170 | 150 | 130 |
Home |Products|Quality Control|News|About Us|Contact Us
+86 133 6380 3091
No.313 East Of Heping Road,Shijiazhuang,China
Copyright © Hebei Aining Welding Consumable Co., Ltd.
All Rights Reserved. Technical Support: Reanod.
E-mail: manager@hbaining.com
Specification: 3.2*350MM, 4.0*400MM
Delivery Time: 10 days
Payment Term: T/T or L/C
E7018 Welding Electrode is an outstanding quality all position welding electrode, covered with extra low hydrogen potassium type, coating for welding high tensile steels and low alloy steels. Its nominal welding efficiency is about 110% due to iron powder is contained. The weld metal shows an excellent low temperature toughness and high crack resistance. Ti is widely used in important projects of ships, boilers, high press vessel, bridges, skyscrapers, offshore drilling platforms, nuclear power stations ect. The groove of base metal should be cleared away impurities, and the electrode must be baked at a temperature to 400 degree, then be held 1-2 hours before welding, 2.5mm one should be done by 350 degree, then be held 1 hour.
The normal sizes: 2.5*300mm, 3.2*350mm, 4.0*400mm, 5.0*450mm.
Chemical Composition of Deposited Metal (%):
| C | Mn | Si | S | P | Cr | Ni | Mo | V | |
| Standard | ≤0.15 | ≤1.60 | ≤0.75 | ≤0.035 | ≤0.040 | ≤0.20 | ≤0.30 | ≤0.30 | ≤0.08 |
| Typical | 0.068 | 1.36 | 0.51 | 0.010 | 0.016 | 0.047 | 0.022 | 0.010 | 0.014 |
Mechanical Properties of Deposited Metal (%)
| Yield Point ReH (Mpa) | Tensile Strength Rm (Mpa) | Elongation A 5 (%) | -20℃(J) | -29℃(J) | -46℃(J) | |
| Standard | ≥375 | 490-660 | ≥22 | ≥47 | ≥27 | ≥27 |
| Gypical | 440 | 540 | 30 | 170 | 150 | 130 |
Home |Products|Quality Control|News|About Us|Contact Us
manager@hbaining.com+86 133 6380 3091
No.313 East Of Heping Road,Shijiazhuang,China
Copyright © Hebei Aining Welding Consumable Co., Ltd. All Rights Reserved. Technical Support: Reanod.