E7018 Welding Electrode

Specification: 3.2*350MM

Delivery Time:10 days

Payment Term: T/T or L/C

Enquire Now

E7018 Welding Electrode is an outstanding quality all position welding electrode, covered with extra low hydrogen potassium type, coating for welding high tensile steels and low alloy steels. Its nominal welding efficiency is about 110% due to iron powder is contained. The weld metal shows an excellent low temperature toughness and high crack resistance. Ti is widely used in important projects of ships, boilers, high press vessel, bridges, skyscrapers, offshore drilling platforms, nuclear power stations ect. The groove of base metal should be cleared away impurities, and the electrode  must be baked at a temperature to 400 degree, then be held 1-2 hours before welding, 2.5mm one should be done by 350 degree, then be held 1 hour.

 

The normal sizes: 2.5*300mm, 3.2*350mm, 4.0*400mm, 5.0*450mm.

 

Chemical Composition of Deposited Metal (%):


C
Mn
Si
S
P
Cr
Ni
Mo
V
Standard≤0.15
≤1.60≤0.75≤0.035≤0.040≤0.20≤0.30≤0.30≤0.08
Typical0.068
1.36
0.51
0.010
0.016
0.047
0.022
0.010
0.014

 

Mechanical Properties of Deposited Metal (%)


Yield Point ReH  (Mpa)Tensile Strength Rm (Mpa)Elongation A 5 (%)-20℃(J)-29℃(J)-46℃(J)
Standard≥375490-660≥22≥47≥27≥27
Gypical440
540
30
170
150
130


LinksWelding Electrode Welding Wire Submerged Arc Welding Wire Flux Cored Welding Wire Welding Torch

HomeProductsNewsAbout UsContact UsSitemap

manager@hbaining.com+86 133 6380 3091No.313 East Of Heping Road,Shijiazhuang,China

Copyright © Hebei Aining Welding Consumable Co., Ltd. All Rights Reserved. Technical Support: Reanod.

Jake Song

Ms.Vicky

Ms.Eva

Tel: +86-311-6669 7109

manager@hbaining.com
Hebei Welding Consumable Supplier
HomeProductsCarbon Steel Welding Electrode
Carbon Steel Welding Electrode Stainless Steel Welding Electrode CO2 Welding Wire Submerged Arc Welding Wire Argon Arc Welding Wire Flux Cored Welding Wire Welding Torch
E7018 Welding Electrode

Product Name: E7018 Welding Electrode

Specification: 3.2*350MM

Delivery Time: 10 days

Payment Term: T/T or L/C

E7018 Welding Electrode is an outstanding quality all position welding electrode, covered with extra low hydrogen potassium type, coating for welding high tensile steels and low alloy steels. Its nominal welding efficiency is about 110% due to iron powder is contained. The weld metal shows an excellent low temperature toughness and high crack resistance. Ti is widely used in important projects of ships, boilers, high press vessel, bridges, skyscrapers, offshore drilling platforms, nuclear power stations ect. The groove of base metal should be cleared away impurities, and the electrode  must be baked at a temperature to 400 degree, then be held 1-2 hours before welding, 2.5mm one should be done by 350 degree, then be held 1 hour.

 

The normal sizes: 2.5*300mm, 3.2*350mm, 4.0*400mm, 5.0*450mm.

 

Chemical Composition of Deposited Metal (%):


C
Mn
Si
S
P
Cr
Ni
Mo
V
Standard≤0.15
≤1.60≤0.75≤0.035≤0.040≤0.20≤0.30≤0.30≤0.08
Typical0.068
1.36
0.51
0.010
0.016
0.047
0.022
0.010
0.014

 

Mechanical Properties of Deposited Metal (%)


Yield Point ReH  (Mpa)Tensile Strength Rm (Mpa)Elongation A 5 (%)-20℃(J)-29℃(J)-46℃(J)
Standard≥375490-660≥22≥47≥27≥27
Gypical440
540
30
170
150
130


Home |Products|Quality Control|News|About Us|Contact Us

+86 133 6380 3091

manager@hbaining.com

No.313 East Of Heping Road,Shijiazhuang,China

Copyright © Hebei Aining Welding Consumable Co., Ltd.

All Rights Reserved. Technical Support: Reanod.

Welding Consumable Supplier

E-mail: manager@hbaining.com

Home Products Quality Control News About Us Contact Us
HomeProductsCarbon Steel Welding Electrode
Carbon Steel Welding Electrode Stainless Steel Welding Electrode CO2 Welding Wire Submerged Arc Welding Wire Argon Arc Welding Wire Flux Cored Welding Wire Welding Torch
E7018 Welding Electrode

Product Name: E7018 Welding Electrode

Specification: 3.2*350MM

Delivery Time: 10 days

Payment Term: T/T or L/C

E7018 Welding Electrode is an outstanding quality all position welding electrode, covered with extra low hydrogen potassium type, coating for welding high tensile steels and low alloy steels. Its nominal welding efficiency is about 110% due to iron powder is contained. The weld metal shows an excellent low temperature toughness and high crack resistance. Ti is widely used in important projects of ships, boilers, high press vessel, bridges, skyscrapers, offshore drilling platforms, nuclear power stations ect. The groove of base metal should be cleared away impurities, and the electrode  must be baked at a temperature to 400 degree, then be held 1-2 hours before welding, 2.5mm one should be done by 350 degree, then be held 1 hour.

 

The normal sizes: 2.5*300mm, 3.2*350mm, 4.0*400mm, 5.0*450mm.

 

Chemical Composition of Deposited Metal (%):


C
Mn
Si
S
P
Cr
Ni
Mo
V
Standard≤0.15
≤1.60≤0.75≤0.035≤0.040≤0.20≤0.30≤0.30≤0.08
Typical0.068
1.36
0.51
0.010
0.016
0.047
0.022
0.010
0.014

 

Mechanical Properties of Deposited Metal (%)


Yield Point ReH  (Mpa)Tensile Strength Rm (Mpa)Elongation A 5 (%)-20℃(J)-29℃(J)-46℃(J)
Standard≥375490-660≥22≥47≥27≥27
Gypical440
540
30
170
150
130


Home |Products|Quality Control|News|About Us|Contact Us

manager@hbaining.com+86 133 6380 3091

No.313 East Of Heping Road,Shijiazhuang,China

Copyright © Hebei Aining Welding Consumable Co., Ltd. All Rights Reserved. Technical Support: Reanod.